Degreasing and phosphating in surface pretreatment

• Précédent
• Suivant

Degreasing and phosphating in surface pretreatment

 Degreasing.
        Phosphating solution excellent phosphate film as long as the workpiece appearance in the oil removed completely to constitute, cleaning agents due to oil residue on the workpiece appearance will not only severely prevent the growth of phosphate film, and will also affect the adhesion of the coating film, drying function, decoration function and corrosion resistance.
         Commonly used degreasers are: strong alkaline degreaser, weak alkaline degreaser, organic solvent degreaser; according to the temperature distinction there are: high temperature, medium temperature, low temperature degreaser.
        Strong alkaline degreaser is rich in a lot of alkali (sodium hydroxide), not easy to clean; in addition, the temperature of the degreaser can not be too high (generally 40 ℃ or so), to avoid drying the workpiece before washing, the formation of phosphate after the phenomenon of rust return.
        Cleaner for the selection of degreasing solution should be fully considered the workpiece appearance of the oil situation, the size of the amount of degreasing agent foam, to avoid excessive foam to form production difficulties or unnecessary waste.
Degreasing station spraying pressure should be higher to ensure the degreasing effect, the general pressure of 0.1 to 0.5mpa. spraying moment control in 2 minutes, to ensure that the degreasing solution and the full reaction of oil.
        Phosphating: phosphating solution
        Phosphating solution so-called phosphating, refers to the metal workpiece through the treatment of acidic solutions rich in dihydrogen phosphate, cleaning agent chemical reaction and generate a layer of stable insoluble or insoluble phosphate film on its surface, the resulting film is called phosphate film. The primary role of phosphate film is: to improve adhesion and add corrosion resistance of the coating.
       Phosphate chemical spraying pressure is too low, easy to form incomplete phosphate; pressure is too high, easy to form a lot of phosphate splash, not conducive to film. General spraying pressure should be controlled at 0.05Mpa, phosphate chemical spraying moment should be controlled in 3 minutes to ensure that the phosphate solution and the substrate of the full reaction to give phosphate film growth of sufficient time to avoid leakage and yellowing phenomenon.